WJ-400E熔体流动速率仪

熔体流动速率仪产品概述

本仪器适用于熔融温度较高的聚乙烯、聚芳砜、氟塑料、尼龙等工程塑料，也适用于聚苯乙烯、聚丙烯、ABS树脂、聚甲醛树脂的熔体流动速率MFR值的测定和各种高聚物在粘流状态时的熔体流动速率值测定，尤其适用于聚丙烯、纳米纤维等高聚物熔喷料的熔体流动速率MVR值测定，可广泛地应用于塑料生产、塑料制品、石油化工等行业以及有关院校、科研单位和商检部门。

熔体流动速率仪符合标准

ISO 1133-1：2011 《Plastics — Determination of the melt mass-flow rate (MFR) and melt volume-flowrate (MVR) of thermoplastics —Part 1:Standard method》

ISO 1133-2：2011 《Plastics — Determination of the melt mass-flow rate (MFR) and melt volume-flowrate (MVR) of thermoplastics —Part 2: Method for materials sensitive to timetemperature history and/or moisture》

GB/T 3682-2018《塑料—热塑性塑料熔体质 量流动速率（MFR）和熔体体积流动速率（MVR）的测定》

ASTM D 1238-10 《Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer》

JB/T 5456-2016 《熔体流动速率仪 技术规范》

熔体流动速率仪产品特点

1、位移采用的分辨率达1um的高精度、高响应的位移传感器，数据采集精准、快速、可靠；

2、温度采集单元采用24bit高精度模数转换器，具有*的温度采样精度和稳定性，温度分辨力达0.01℃；

3、系统升温速度快，恒温精度高，填料后温度恢复时间短，2min内可迅速恢复到恒温状态，温度控制稳定可靠；

4、 采用双PID 分段加热的控制方式对炉体进行精确合理的热量分配，炉体温度均匀度小于±0.3℃；

5、毫秒级数据采集间隔，高速捕捉材料的位移变化，可精准测试高达5000cm³/10min高流速材料的熔融指数；

6、采用7寸全彩色液晶触摸屏控制终端，具备中、英等多国语言界面，使用便捷；

7、系统可自动识别国标、ISO标准以及美标的有效测试区间；

8、控制软件可实现参数的设定、恒温控制、计量校准、定时等功能；测定规定时间试样的MVR值，输入熔融密度后系统自动得出MFR值；

9、配有PC机软件，通过软件可对移动存储设备的试验数据进行处理，生成试验报告。

10、口模塞装置采用扳把连杆式传动机构，定位准确，密封可靠，操作简单；

熔体流动速率仪技术参数

1、测量方法：质量法、体积法；

2、测量范围：(0.01～5000)g/10min、1cm³/10min～5000cm³/10min；

3、控温范围：室温～450℃；

4、温度显示分辨力：0.01℃；

5、温度示值偏差：≤±0.01℃；

6、温度波动度：≤±0.1℃；

7、计时分辨力：0.01s；

8、温度恢复时间：≤3min；

9、炉体温度均匀度：±0.2℃；

10、活塞位移显示分辨力：0.001mm；

11、活塞位移示值偏差：满量程范围内≤±0.01mm；

12、砝码质量偏差：±0.1%；

13、电源：220(1-15%)VAC～220(1+10%)VAC 50Hz 0.5kVA 单相三线；

14、主机尺寸（长×宽×高）： 550mm×430mm ×650mm ；

15、主机重量：约62kg。

Product name: XNR - 400 - b melt flow rate meter
Application industry: polyethylene, polypropylene, pom, ABS resin, polycarbonate, nylon, fluorine plastic polymer, etc
Test items: melt index （melt flow index） plastic polymer liquid
Main application:
Melt flow rate meter is also called the melt index instrument is according to GB/T 3682 test method, liquid at high temperature is used for testing thermoplastic polymer melt mass flow rate （MFR; unit: g / 10 min）, such as polyethylene, polypropylene, pom, ABS resin, polycarbonate, nylon, fluorine plastic polymer, etc.Widely used in plastic production, plastic products, petrochemical and other industries as well as universities and colleges, scientific research units, the commodity inspection department.The equipment is performing to standard JB/T5456 requirements and applicable standards such as GB/T3682, ISO1133, widely used in the determination of plastic melt index value.
Function characteristics:
1, LCD screen display operation platform, full Chinese menu system.
2, blanking method in manual and automatic control, the three set arbitrary.  
3, can print test reports..
Technical parameters:
Measurement method: quality standard （MFR）
Constant temperature range: room temperature - 450 ℃
Temperature accuracy: plus or minus 0.2 ℃
The temperature resolution: 0.1 ℃
Timing range: 0.1-999 seconds
Timing accuracy: 0.1 seconds
Discharging mouth diameter: Φ 2.095 + / - 0.005 mm
The discharging mouth length: 8.000 + / - 0.025 mm
Charging tube diameter: Φ 9.550 + / - 0.025 mm
Charging barrel length: 152 + / - 0.1 mm
The piston rod head diameter: 9.475 + / - 0.015 mm
8 standard test load （total weight）
Main configuration: host a full range of magnitude 8 farmar mouth mold pour material lever feed hopper cleaning rod piston rod